High Saturation Soft Magnetic Alloys VACOFLUX 27 for High Performance Actuator Systems

VACOFLUX 27 High Saturation Magnetic Alloy for High Performance Actuator Systems

VACOFLUX 27 offers the highest saturation of all Fe-Co alloys. What's more, it shows an excellent ductility. It is available as hot-rolled, forged bars, cold rolled strips as well as cold drawn wire. Due to the relatively low electrical resistivity, it is commonly used for static applications.

Density: 7.95 g/cm³
Electrical resistivity:19 µΩ - cm
Curie temperature: 925°C
Saturation magnetostriction: 36x10^-6
Saturation induction: 23.6kG (2.36T)
Modulus of elasticity: 24 × 10⁶psi (166GPa)
Thermal conductivity: 54.8 W/m·K
Thermal expansivity, 10^-6/°C

Applications

Back irons, pole pieces and other flux guiding elements, high power electromagnetic actuators and hydraulic or pneumatic systems

Mainly applications with static fields.

Chemical composition

All stamped laminations or machined part must be magnetic annealed after fabrication to develop acceptable magnetic properties.

Anneal part at 760-900°C for 2 to 4 hours in dry hydrogen or vacuum at cool at 80-300°C/h to 300°C

All parts must be cleaned before annealing.

soft ferromagnetic materials

soft iron material